Chromium-molybdenum ferrum iaciens late in campis industrialibus cum proprietatibus mechanicis relative utitur.Additio molybdeni ad chromium chalybem vires augere potestferro dejectionessine ictu notabili ictum habens duritiem injecto ferro.Praeterea, chromium-molybdaeum missum chalybem optimam caliditatem exercendi habet et resistentiam repunt.Postquam exstingui et temperare vel normali curationis aestus, chromium-molybdaeum eiectum chalybem optimas proprietates mechanicas obtinere potest.
Molybdenum duritiem ferri dejecti emendare potest, et ingenium fragilitatem fusi ferri minuere.Chromium-molybdaenum emissum chalybeum adhibitum estmagna-sectione dejectioneset chalybea flatura alta duritia requirunt.
Chemical Composition of Chrome Molybdenum Cast Steel | ||||||
Steel Gradus | C (%) | Si (%) | Mn (%) | Cr (%) | Mo (%) | P、S (%) |
ZG20CrMo | 0.17-0.25 | 0.20-0.45 | 0.50-0.80 | 0.50-0.80 | 0.40-0.60 | ≤0.035 |
ZG35CrMo | 0.30-0.37 | 0.30-0.50 | 0.50-0.80 | 0.80-1.20 | 0.20-0.30 | ≤0.035 |
ZG40CrMo | 0.35-0.45 | 0.17-0.45 | 0.50-0.80 | 0.80-1.10 | 0.20-0.30 | ≤0.04 |
ZG20Cr5Mo | 0.15-0.25 | ≤0.50 | ≤0.60 | 4.00-6.00 | 0.50-0.65 | ≤0.04 |
ZG17CrMo | 0.15-0.20 | 0.30-0.60 | 0.50-0.80 | 1.20-1.50 | 0.45-0.55 | ≤0.04 |