Medium et stannum chalyberum infimum magnum globulum stannum ferro cum elementis commixtis (elementa maxime chemica ut pii, manganesum, chromium, molybdenum, nickel, cuprum et vanadium) contenta minus quam 8%.Medium et humilis mixturae ferri iniectiones bonam duritiem habent, et bonae proprietates mechanicae comprehensivae post proprium calorem curationis obtineri possunt.
Tractatio Caloris Specificationes de Minimum et Medium Alloy Steel Castings
| |||||
Gradus | Categoria ferro | Specificationes caloris curatio | |||
Curatio Methodi | Temperatus / | Refrigerationem Methodo | duritia / HBW | ||
ZG16Mn | Manganum Ferro | Normalising | 900 | Refrigerant in aere | / |
Temperatio | 600 | ||||
ZG22Mn | Manganum Ferro | Normalising | 880 - 900 | Refrigerant in aere | 155 |
Temperatio | 680 - 700 | ||||
ZG25Mn | Manganum Ferro | Annealing vel Tempering | / | / | 155 - 170 |
ZG25Mn2 | Manganum Ferro | 200 - 250 | |||
ZG30Mn | Manganum Ferro | 160 - 170 | |||
ZG35Mn | Manganum Ferro | Normalising | 850 - 860 | Refrigerant in aere | / |
Temperatio | 560 - 600 | ||||
ZG40Mn | Manganum Ferro | Normalising | 850 - 860 | Refrigerant in aere | 163 |
Temperatio | 550 - 600 | Frigus in fornace | |||
ZG40Mn2 | Manganum Ferro | Annealing | 870 - 890 | Frigus in fornace | 187 - 255 |
exstingui | 830 - 850 | Tepescunt oleum | |||
Temperatio | 350 - 450 | Refrigerant in aere | |||
ZG45Mn | Manganum Ferro | Normalising | 840 - 860 | Refrigerant in aere | 196 - 235 |
Temperatio | 550 - 600 | Frigus in fornace | |||
ZG45Mn2 | Manganum Ferro | Normalising | 840 - 860 | Refrigerant in aere | ≥ 179 |
Temperatio | 550 - 600 | Frigus in fornace | |||
ZG50Mn | Manganum Ferro | Normalising | 860 - 880 | Refrigerant in aere | 180 - 220 |
Temperatio | 570 - 640 | Frigus in fornace | |||
ZG50Mn2 | Manganum Ferro | Normalising | 850 - 880 | Refrigerant in aere | / |
Temperatio | 550 - 650 | Frigus in fornace | |||
ZG65Mn | Manganum Ferro | Normalising | 840 - 860 | / | 187 - 241 |
Temperatio | 600 - 650 | ||||
ZG20SiMn | Silico-Manganese Steel | Normalising | 900 - 920 | Refrigerant in aere | 156 |
Temperatio | 570 - 600 | Frigus in fornace | |||
ZG30SiMn | Silico-Manganese Steel | Normalising | 870 - 890 | Refrigerant in aere | / |
Temperatio | 570 - 600 | Frigus in fornace | |||
exstingui | 840 - 880 | Frigus in oleo / aqua | / | ||
Temperatio | 550 - 600 | Frigus in fornace | |||
ZG35SiMn | Silico-Manganese Steel | Normalising | 860 - 880 | Refrigerant in aere | 163 - 207 |
Temperatio | 550 - 650 | Frigus in fornace | |||
exstingui | 840 - 860 | Tepescunt oleum | 196 - 255 | ||
Temperatio | 550 - 650 | Frigus in fornace | |||
ZG45SiMn | Silico-Manganese Steel | Normalising | 860 - 880 | Refrigerant in aere | / |
Temperatio | 520 - 650 | Frigus in fornace | |||
ZG20MnMo | Manganese Molybdenum Steel | Normalising | 860 - 880 | / | / |
Temperatio | 520 - 680 | ||||
ZG30CrMnSi | Chromium Manganese Silicon Steel | Normalising | 800 - 900 | Refrigerant in aere | 202 |
Temperatio | 400 - 450 | Frigus in fornace | |||
ZG35CrMnSi | Chromium Manganese Silicon Steel | Normalising | 800 - 900 | Refrigerant in aere | ≤ 217 |
Temperatio | 400 - 450 | Frigus in fornace | |||
Normalising | 830 - 860 | Refrigerant in aere | / | ||
830 - 860 | Tepescunt oleum | ||||
Temperatio | 520 - 680 | Refrigerant in aere / fornacis | |||
ZG35SiMnMo | Silico-manganese-molybdaenum chalybe | Normalising | 880 - 900 | Refrigerant in aere | / |
Temperatio | 550 - 650 | Refrigerant in aere / fornacis | |||
exstingui | 840 - 860 | Tepescunt oleum | / | ||
Temperatio | 550 - 650 | Frigus in fornace | |||
ZG30Cr | Chrome Steel | exstingui | 840 - 860 | Tepescunt oleum | ≤ 212 |
Temperatio | 540 - 680 | Frigus in fornace | |||
ZG40Cr | Chrome Steel | Normalising | 860 - 880 | Refrigerant in aere | ≤ 212 |
Temperatio | 520 - 680 | Frigus in fornace | |||
Normalising | 830 - 860 | Refrigerant in aere | 229 - 321 | ||
exstingui | 830 - 860 | Tepescunt oleum | |||
Temperatio | 525 - 680 | Frigus in fornace | |||
ZG50Cr | Chrome Steel | exstingui | 825 - 850 | Tepescunt oleum | ≥ 248 |
Temperatio | 540 - 680 | Frigus in fornace | |||
ZG70Cr | Chrome Steel | Normalising | 840 - 860 | Refrigerant in aere | ≥ 217 |
Temperatio | 630 - 650 | Frigus in fornace | |||
ZG35SiMo | Silicon Molybdenum Steel | Normalising | 880 - 900 | / | / |
Temperatio | 560 - 580 | ||||
ZG20Mo | Molybdenum Steel | Normalising | 900 - 920 | Refrigerant in aere | 135 |
Temperatio | 600 - 650 | Frigus in fornace | |||
ZG20CrMo | Chrome-molybdenum chalybeum | Normalising | 880 - 900 | Refrigerant in aere | 135 |
Temperatio | 600 - 650 | Frigus in fornace | |||
ZG35CrMo | Chrome-molybdenum chalybeum | Normalising | 880 - 900 | Refrigerant in aere | / |
Temperatio | 550 - 600 | Frigus in fornace | |||
exstingui | 850 | Tepescunt oleum | 217 | ||
Temperatio | 600 | Frigus in fornace |
Characteres caloris curationis Medii et Low Alloy Steel Castings:
1. Medium et humilis mixturae ferri iniectiones plerumque adhibentur in machinationibus industriis ut autocineta, obtrectatores, impedimenta, machinamenta fabricandi et systemata hydraulica.Hae industriae iactationes cum viribus et duritia requirunt.Ad fusuras distrahentes vires minus 650 MPa postulantes, normalizing + temperamentum caloris adhibendum est;ad mixturam ferri media et infima iactantia quae distrahentes vim maiorem quam 650 MPa requirunt, exstinguiendi + caliditas temperaturae caloris curatio adhibenda est.Post extinctionem et temperantiam, metallurgicae compages ex ferro dejectione sorbitarum temperatur, ad obtinendum altiorem vim et duritiem bonam.Sed quando figura et magnitudo eiectionis non sunt idoneae ad restinguendum, normalizing + temperamentum adhibendum est pro restinguendo et temperando.
2. Melius est praetractationem temperare et temperantiam mediae et infimae iactationis ferreae temperare vel ordinare + praetractationem exstinguere.Hoc modo cristallum granum ferri deiectio depurari potest et structura uniformis, ut effectum finalem exstinguiendi et temperandi curationem augens, et etiam adiuvans ad vitandum effectus adversos effectus emissionis intra dejectionem.
3. Post exstinguendam curationem, mixturae mediae et infimae ferro iactaturae martensitae structuram quam maxime obtinere debent.Ad hoc propositum assequendum, medium exstingui temperatura et infrigidatio eligenda est secundum gradus ferreos proiectos, duritiem, parietum crassitudinem, figuram et alia elementa.
4. Ut ad exstinguiendam fusti ferrum structuram accommodes et accentus restinguendam exstinguendum, mediae et infimae infixionis ferrum statim post extinctionem temperari debent.
5. Sub praemissis viribus ferri non minuendi, medium carbonis depressum admixtum, altum robur ferri vis indurari potest.Durior curatio plasticitatem et duritiem fusurarum ferri potest emendare.
Temperatus et duritia of Low Alloy Steel post QT Calor curatio
| |||
Humilis et medium Alloy Steel Grade | Exstingui Temperature / | Temperature Temperature / | duritia / HBW |
ZG40Mn2 | 830 - 850 | 530 - 600 | 269 - 302 |
ZG35Mn | 870 - 890 | 580 - 600 | ≥ 195 |
ZG35SiMnMo | 880 - 920 | 550 - 650 | / |
ZG40Cr1 | 830 - 850 | 520 - 680 | / |
ZG35Cr1Mo | 850 - 880 | 590 - 610 | / |
ZG42Cr1Mo | 850 - 860 | 550 - 600 | 200 - 250 |
ZG50Cr1Mo | 830 - 860 | 540 - 680 | 200 - 270 |
ZG30CrNiMo | 860 - 870 | 600 - 650 | ≥ 220 |
ZG34Cr2Ni2Mo | 840 - 860 | 550 -600 | 241 - 341 |
Post tempus: Iul-31-2021