Consuetudo ferrea jactans glaucum emittere partes byharenae formam mittentesetCNC subtilitas machiningprocessibus. OEM customized engineering services are also available.
Facultates de Arena per manum fundendi efficta;
• Max Size: 1,500 mm × 1000 mm × 500 mm
• Pondus dolor: 0.5 kg - 500 kg
• Capacitas annua: 5,000 tons - 6,000 tons
• Tolerantiae: In Request or Standard (ISO8062-2013 or Chinese Standard GB/T 6414-1999)
• Mola Materias: Viridis Arenam Iactis, Testa Mola Arena Iactans.
Capabilities of Sand Casting by Automatic Molding Machines:
• Max Size: 1,000 mm × 800 mm × 500 mm
• Pondus dolor: 0.5 kg - 500 kg
• Capacitas annua: 8,000 tons - 10,000 tons
• Tolerantiae: De Request vel Secundum Latin (ISO8062-2013 or Chinese Standard GB/T 6414-1999)
• Materias Molde: Arenam Viridis Iactans, Resinam Coated Arenam Testam CUMATIUM Iaculans.
Theharenae formam mittentes liquaturat RMC instructa laboratorio metallurgico perfecto ad determinandas notas chemicas et mechanicas uniuscuiusque liquefactionis, et ad resolvendum conditionem metallurgicam metalli fusilis ante infusionem. Microsectiones sub microscopio examinantur ut notitias finales obtineat. Si fieri potest vel opus fuerit, 3.1 Certificatorium pro unaquaque parte traditionis in petitione clientium statuere possumus.
Arena products dejectiopossem in *multae industriesut Tympana, Apparatus, Apparatus Praesent, Mining Machinery, Adscendens Clausus, Hydraulic Pressura Pump, Ferens Sedem, Suscipe Annulo, Otiosa Rota, Fibulae, Adscendens Bracket, Rota Hub, Cuneum Socket, Track Pad enim Mining Equipment, Hydraulic Rod Jugum .. .etc.
| Mechanica proprietatibus Gray | |||||||
| Item secundum DIN EN 1561 | mensura | Unitas | EN-GJL-150 | EN-GJL-200 | EN-GJL-250 | EN-GJL-300 | EN-GJL-350 |
| EN-JL 1020 | EN-JL 1030 | EN-JL 1040 | EN-JL 1050 | EN-JL 1060 | |||
| distrahentes Fortitudo | Rm | MPA | 150-250 | 200-300 | 250-350 | 300-400 | 350-450 |
| 0,1% cede virtus | Rp0,1 | MPA | 98-165 | 130-195 | 165-228 | 195-260 | 228-285 |
| Prolongatio Fortitudo | A | % | 0,3 - 0,8 | 0,3 - 0,8 | 0,3 - 0,8 | 0,3 - 0,8 | 0,3 - 0,8 |
| Compressive fortitudo | σdB | MPa | 600 | 720 | 840 | 960 | 1080 |
| 0,1% Compressive virtus | σd0,1 | MPa | 195 | 260 | 325 | 390 | 455 |
| Flexurae Fortitudo | σbB | MPa | 250 | 290 | 340 | 390 | 490 |
| Schuifspanning | σB | MPa | 170 | 230 | 290 | 345 | 400 |
| tondendas Suspendisse | TtB | MPa | 170 | 230 | 290 | 345 | 400 |
| Modi elasticitates | E | GPa | 78 – 103 | 88 – 113 | 103 – 118 | 108 – 137 | 123 – 143 |
| Pisces numero | v | - | 0,26 | 0,26 | 0,26 | 0,26 | 0,26 |
| Brinell duritia | HB | 160 – 190 | 180 – 220 | 190 – 230 | 200 – 240 | 210 – 250 | |
| Ductility | σbW | MPa | 70 | 90 | 120 | 140 | 145 |
| Tensio et pressura mutatio | σzdW | MPa | 40 | 50 | 60 | 75 | 85 |
| Fortitudo praevaricationem | Klc | N/mm3/2 | 320 | 400 | 480 | 560 | 650 |
| Densitas | g/cm3 | 7,10 | 7,15 | 7,20 | 7,25 | 7,30 | |
Ferrum missum est carbonis stannum ferreum missum cum aliis elementis, quae fit ex ferro porcino, faece, et aliis additamentis. Ad differentia- tionem ex ferro et chalybe abjecto, ferrum conjectum ut mixtura carbonis contentum (min 2.03%) efficit, quae solidificationem periodi nalis cum eutectica transformatione efficit. Fretus in speciebus chemicis, ferrum conjectum non commixtum vel mixtum esse potest. Ferrorum commixtio multo latior est, quae vel superiora pondera communia, ut pii et manganesum, vel peculiares additiones, ut nickel, chromium, aluminium, molybdenum, tungstenum, cuprum, vana- dium, titanium, plus. alii. Fere ferrum fusum dividi poterat in ferrum griseum, ducitle ferrum (ferrum nodulare), ferrum album, graphite ferrum compactum et malleabile ferrum conjecit.